THE ROLE OF HIGH-PRESSURE SINTERING IN PREPARING HIGH-QUALITY N-TYPE ND2-XCEXCUO4-Y SUPERCONDUCTORS | |
C. Q. Jin; W. L. Zhou; H. Gu; Y. S. Yao; W. K. Wang | |
1993 | |
发表期刊 | Journal of Applied Physics
![]() |
ISSN | 0021-8979 |
卷号 | 73期号:2页码:843-849 |
摘要 | High-pressure high-temperature sintering (HHS) under 1.0, 2.0, 4.0, and 6.0 GPa for a short time was directly used to reduce n-type Nd1.85Ce0.15CuO4-y. Superconductors with higher critical temperature were obtained. The samples display lower resistivity, and more metalliclike resistance behavior at normal state with increasing sintering pressure. A small increase of lattice parameter and cell volume was observed via electron and x-ray diffraction. Transmission electron microscopy studies also show that there is a preferential orientation along the c axis among the neighboring grains. This helps get well-matching grain boundaries in the HHS samples. A Cu2O high-pressure phase was found via energy-dispersive x-ray analysis in the sample treated above 5.0 GPa, which is thought to be a deleterious factor for superconductivity. Sintering under suitable pressure not only enhances the intragranular conductivity, but also effectively improves the intergranular links. Finally, via the assumed interstitial oxygen ordering in the T' structure, a possible mechanism of n-type reduction is proposed based on the change in tolerance factor under reduction atmosphere and high pressure. |
部门归属 | chinese acad sci,beijing electron microscopy lab,beijing 100080,peoples r china. chinese acad sci,natl lab supercond,beijing 100080,peoples r china. acad sinica,int ctr mat phys,shenyang 110015,peoples r china.;jin, cq (reprint author), chinese acad sci,inst phys,beijing 100080,peoples r china |
关键词 | Cu-o System Quasihydrostatic Pressure Transition Nd1.85ce0.15cuo4-delta Temperature Transport Compound Crystals Oxygen Growth |
URL | 查看原文 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.imr.ac.cn/handle/321006/39046 |
专题 | 中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | C. Q. Jin,W. L. Zhou,H. Gu,et al. THE ROLE OF HIGH-PRESSURE SINTERING IN PREPARING HIGH-QUALITY N-TYPE ND2-XCEXCUO4-Y SUPERCONDUCTORS[J]. Journal of Applied Physics,1993,73(2):843-849. |
APA | C. Q. Jin,W. L. Zhou,H. Gu,Y. S. Yao,&W. K. Wang.(1993).THE ROLE OF HIGH-PRESSURE SINTERING IN PREPARING HIGH-QUALITY N-TYPE ND2-XCEXCUO4-Y SUPERCONDUCTORS.Journal of Applied Physics,73(2),843-849. |
MLA | C. Q. Jin,et al."THE ROLE OF HIGH-PRESSURE SINTERING IN PREPARING HIGH-QUALITY N-TYPE ND2-XCEXCUO4-Y SUPERCONDUCTORS".Journal of Applied Physics 73.2(1993):843-849. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论