Structural, mechanical and corrosion studies of Cr-rich inclusions in 152 cladding of dissimilar metal weld joint

IMR OpenIR

	Structural, mechanical and corrosion studies of Cr-rich inclusions in 152 cladding of dissimilar metal weld joint
	Li, YF; Wang, JQ; Han, EH; Yang, CD; Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China.
	2018
发表期刊	JOURNAL OF NUCLEAR MATERIALS
ISSN	0022-3115
卷号	498 页码:9-19
摘要	Cr-rich inclusions were discovered in 152 cladding at the inner wall of domestic dissimilar metal weld joint, and their morphologies, microstructures, mechanical properties and corrosion behaviors were systematically characterized by SEM, TEM, nanoindentation and FIB. The results indicate that the Cr-rich inclusions originate from large-size Cr particles in 152 welding electrode flux, and they are 50-150 mm in size in most cases, and there is a continuous transition zone of 2-5 mm in width between the Cr inclusion core and 152 cladding matrix, and the transition zone consists of Ni & Fe-rich dendritic austenite and Cr23C6 and Cr matrix. The transition zone has the highest nanoindentation hardness (7.66 GPa), which is much harder than the inclusion core (5.14 GPa) and 152 cladding (3.71 GPa). In-situ microscopic tensile tests show that cracks initialize preferentially in transition zone, and then propagate into the inclusion core, and creep further into 152 cladding after penetrating the core area. The inclusion core and its transition zone both share similar oxide film structure with nickel-base 152 cladding matrix in simulated primary water, while those two parts present better general corrosion resistance than 152 cladding matrix due to higher Cr concentration. (C) 2017 Elsevier B.V. All rights reserved.; Cr-rich inclusions were discovered in 152 cladding at the inner wall of domestic dissimilar metal weld joint, and their morphologies, microstructures, mechanical properties and corrosion behaviors were systematically characterized by SEM, TEM, nanoindentation and FIB. The results indicate that the Cr-rich inclusions originate from large-size Cr particles in 152 welding electrode flux, and they are 50-150 mm in size in most cases, and there is a continuous transition zone of 2-5 mm in width between the Cr inclusion core and 152 cladding matrix, and the transition zone consists of Ni & Fe-rich dendritic austenite and Cr23C6 and Cr matrix. The transition zone has the highest nanoindentation hardness (7.66 GPa), which is much harder than the inclusion core (5.14 GPa) and 152 cladding (3.71 GPa). In-situ microscopic tensile tests show that cracks initialize preferentially in transition zone, and then propagate into the inclusion core, and creep further into 152 cladding after penetrating the core area. The inclusion core and its transition zone both share similar oxide film structure with nickel-base 152 cladding matrix in simulated primary water, while those two parts present better general corrosion resistance than 152 cladding matrix due to higher Cr concentration. (C) 2017 Elsevier B.V. All rights reserved.
部门归属	[li, yifeng ; wang, jianqiu ; han, en-hou] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, liaoning, peoples r china ; [li, yifeng] univ sci & technol china, sch mat sci & engn, shenyang 110016, liaoning, peoples r china ; [yang, chengdong] shanghai res ctr weld & detect engn tech nucl equ, shanghai 201306, peoples r china
关键词	Pressurized-water Reactors Environmentally-assisted Cracking Safe-end Quantitative Assessment Secondary-side Residual-stresses High-temperature Fusion Boundary Base Alloys Part 1
学科领域	Materials Science, Multidisciplinary ; Nuclear Science & Technology
资助者	National Key Research and Development Program of China [2016YFB0300401, 2016YFE0105200]; Key Research Program of Frontier Sciences, Chinese Academy of Sciences [QYZDY-SSW-JSC012]
收录类别	SCI
语种	英语
WOS记录号	WOS:000418472300002
引用统计	被引频次：8[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79618
专题	中国科学院金属研究所
通讯作者	Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Li, YF,Wang, JQ,Han, EH,et al. Structural, mechanical and corrosion studies of Cr-rich inclusions in 152 cladding of dissimilar metal weld joint[J]. JOURNAL OF NUCLEAR MATERIALS,2018,498:9-19.
APA	Li, YF,Wang, JQ,Han, EH,Yang, CD,&Wang, JQ .(2018).Structural, mechanical and corrosion studies of Cr-rich inclusions in 152 cladding of dissimilar metal weld joint.JOURNAL OF NUCLEAR MATERIALS,498,9-19.
MLA	Li, YF,et al."Structural, mechanical and corrosion studies of Cr-rich inclusions in 152 cladding of dissimilar metal weld joint".JOURNAL OF NUCLEAR MATERIALS 498(2018):9-19.