| Solvothermal Synthesis of Size-controlled Lead Zirconate Titanate Particles |
| F.; Wang Zhang, Z. J.
|
| 2014
|
| 发表期刊 | Environmental Technology and Resource Utilization Ii
 |
| ISSN | 1660-9336
|
| 卷号 | 675-677页码:27-30 |
| 摘要 | Nanocrystalline lead zirconate titanate (PZT) powders have been synthesized by solvothermal method, in which a mixed solvent of ethanol and water was used as reactive medium and Pb(NO3)(2), ZrOCl2 center dot 8H(2)O, C16H36O4Ti, KOH and NH3 center dot H2O were used as raw materials. It was found that PZT particle sizes decreased from 2 mu m to 100 nm with the ratio of V-ethanol/V-water increasing from 1/2 to 2/1 under a KOH concentration of 4 mol/L at 200 degrees C for 4 h. It indicated that the V-ethanol/V-water of mixed solvent played an important role in controlling the morphology and size of PZT crystals, as well as reaction temperature. |
| 部门归属 | [zhang, fan
; wang, zhanjie] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, liaoning, peoples r china.
; zhang, f (reprint author), chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, liaoning, peoples r china.
; zhangfan7357@163.com
; wangzj@imr.ac.cn
|
| 关键词 | Size-controlled
Solvothermal
Lead Zirconate Titanate
|
| URL | 查看原文
|
| 文献类型 | 期刊论文
|
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/74016
|
| 专题 | 中国科学院金属研究所
|
推荐引用方式
GB/T 7714 |
F.,Wang Zhang, Z. J.. Solvothermal Synthesis of Size-controlled Lead Zirconate Titanate Particles[J]. Environmental Technology and Resource Utilization Ii,2014,675-677:27-30.
|
| APA |
F.,&Wang Zhang, Z. J..(2014).Solvothermal Synthesis of Size-controlled Lead Zirconate Titanate Particles.Environmental Technology and Resource Utilization Ii,675-677,27-30.
|
| MLA |
F.,et al."Solvothermal Synthesis of Size-controlled Lead Zirconate Titanate Particles".Environmental Technology and Resource Utilization Ii 675-677(2014):27-30.
|
修改评论