Microstructure evolution and its influence on deformation mechanisms during tensile creep of DD417G alloy

IMR OpenIR

	Microstructure evolution and its influence on deformation mechanisms during tensile creep of DD417G alloy
	H. H.; Hou Shi, J. S.; Guo, J. T.; Zhou, L. Z.; Maldini, M.; Angella, G.; Donnini, R.; Ripamonti, D.
	2014
发表期刊	Materials Research Innovations
ISSN	1432-8917
卷号	18 页码:319-323
摘要	In this paper, the variation of gamma prime precipitates along the creep specimen from the end to the fracture surface was studied, on which a necking phenomenon was observed. The morphologies and chemical compositions of gamma prime precipitates of crept DD417G alloy under the condition of 1000 degrees C/115 MPa were studied using scanning electron microscopy ( SEM), transmission electron microscopy (TEM), scanning TEM, with energy diffraction spectrum and Xray diffraction. The results indicate that with a negative gamma/gamma prime lattice misfit the superalloy gamma prime rafted structure formed perpendicular to the tensile loading axis, but in the necked zone, the gamma prime rafts are thickened significantly and no longer perpendicular to the tensile loading axis, but tend to parallel to the tensile loading axis. Based on element diffusion and lattice rotation theories, this phenomenon was discussed. From the observation and analysis of dislocation configurations, it is evident that the tertiary creep deformation is mainly controlled by dislocation shearing mechanism. And, some gamma' particles also precipitate from the matrix during the creep test.
部门归属	[shi, h. h. ; hou, j. s. ; guo, j. t. ; zhou, l. z.] chinese acad sci, inst met res, shenyang 110016, peoples r china. [maldini, m. ; angella, g. ; donnini, r. ; ripamonti, d.] icnr ieni, i-20125 milan, italy. ; zhou, lz (reprint author), chinese acad sci, inst met res, shenyang 110016, peoples r china. ; lzz@imr.ac.cn
关键词	Nickel Based Superalloy Single Crystal Creep Microstructure Evolution Rafts Nickel-base Superalloy Single-crystal Superalloy Temperature Creep Nasair 100 Behavior Morphology Stress
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/73911
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	H. H.,Hou Shi, J. S.,Guo, J. T.,et al. Microstructure evolution and its influence on deformation mechanisms during tensile creep of DD417G alloy[J]. Materials Research Innovations,2014,18:319-323.
APA	H. H..,Hou Shi, J. S..,Guo, J. T..,Zhou, L. Z..,Maldini, M..,...&Ripamonti, D..(2014).Microstructure evolution and its influence on deformation mechanisms during tensile creep of DD417G alloy.Materials Research Innovations,18,319-323.
MLA	H. H.,et al."Microstructure evolution and its influence on deformation mechanisms during tensile creep of DD417G alloy".Materials Research Innovations 18(2014):319-323.