Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition

IMR OpenIR

	Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition
	C. Thee; L. Hao; J. H. Dong; X. Mu; X. Wei; X. F. Li; W. Ke
	2014
发表期刊	Corrosion Science
ISSN	0010-938X
卷号	78 页码:130-137
摘要	Electrochemical Impedance Spectroscopy (EIS) and film thickness measurements have been employed to study the corrosion monitoring of steel under an electrolyte film in wet-dry cycles simulating a coastal atmosphere. The results indicate that within each cycle, the corrosion rate increases during drying process due to an increase in Cl- concentration and an enhancement of oxygen diffusion by thinning out of the electrolyte. As corrosion process proceeds, the corrosion rate increases greatly and reaches a maximum. During subsequent corrosion stage, the corrosion rate decreases greatly and keeps at a low value due to the formation of a stable rust layer. (C) 2013 Elsevier Ltd. All rights reserved.
部门归属	[thee, ch. ; hao, long ; dong, junhua ; mu, xin ; wei, xin ; li, xiaofang ; ke, wei] chinese acad sci, state key lab corros & protect, inst met res, shenyang 110016, peoples r china. ; dong, jh (reprint author), chinese acad sci, state key lab corros & protect, inst met res, wencui rd 62, shenyang 110016, peoples r china. ; chinahaolong@126.com ; jhdong@imr.ac.cn
关键词	Low Alloy Steel Eis Weight Loss Atmospheric Corrosion Rust Carbon-steel Impedance Measurements Anodic Processes Layers Iron Thin Environment Evolution Polarization Performance
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/72327
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	C. Thee,L. Hao,J. H. Dong,et al. Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition[J]. Corrosion Science,2014,78:130-137.
APA	C. Thee.,L. Hao.,J. H. Dong.,X. Mu.,X. Wei.,...&W. Ke.(2014).Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition.Corrosion Science,78,130-137.
MLA	C. Thee,et al."Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition".Corrosion Science 78(2014):130-137.