	Comparison between the oxidation of iron in oxygen and in steam at 650-750 degrees C
	J. T. Yuan; W. Wang; S. L. Zhu; F. H. Wang
	2013
发表期刊	Corrosion Science
ISSN	0010-938X
卷号	75 页码:309-317
摘要	Oxidation of iron was investigated in oxygen and in steam at 650-750 degrees C by TGA, OM, SEM, and XRD. In oxygen, parabolic kinetics and multilayer oxide scales composed of typical three iron oxides were observed. Noticeably, the scale adhesion was very poor. In steam, linear-parabolic shape kinetics and multilayer oxide scales with fewer pores were found. As indicated by Pt marking, inward-growing process in steam was considered to result in the improvement of scale contact. Based on the experimental results, scaling mechanism of iron in steam was discussed. (C) 2013 Elsevier Ltd. All rights reserved.
部门归属	[yuan, juntao ; wang, wen ; zhu, shenglong ; wang, fuhui] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; wang, w (reprint author), chinese acad sci, inst met res, state key lab corros & protect, 62 wencui rd, shenyang 110016, peoples r china. ; jtyuan@imr.ac.cn ; wen@imr.ac.cn ; slzhu@imr.ac.cn ; fhwang@imr.ac.cn
关键词	Iron Sem Xrd High Temperature Corrosion Oxidation High-temperature Oxidation Low-carbon Steel Water-vapor Multicomponent Gases Reaction-mechanisms Behavior Alloys Atmospheres Mixtures Metals
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/71660
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	J. T. Yuan,W. Wang,S. L. Zhu,et al. Comparison between the oxidation of iron in oxygen and in steam at 650-750 degrees C[J]. Corrosion Science,2013,75:309-317.
APA	J. T. Yuan,W. Wang,S. L. Zhu,&F. H. Wang.(2013).Comparison between the oxidation of iron in oxygen and in steam at 650-750 degrees C.Corrosion Science,75,309-317.
MLA	J. T. Yuan,et al."Comparison between the oxidation of iron in oxygen and in steam at 650-750 degrees C".Corrosion Science 75(2013):309-317.