Nanocrystalline Surface Layer on AISI 52100 Steel Induced by Supersonic Fine Particles Bombarding

IMR OpenIR

	Nanocrystalline Surface Layer on AISI 52100 Steel Induced by Supersonic Fine Particles Bombarding
	L. Y. Kong; Y. X. Lao; T. Y. Xiong; T. F. Li
	2013
发表期刊	Journal of Thermal Spray Technology
ISSN	1059-9630
卷号	22 期号:6 页码:1007-1013
摘要	Surface treatment of AISI 52100 steel by supersonic fine particles bombarding (SFPB) was studied in this article. The surface topography, morphology of the surface layer, and microhardness distribution of the surface layer have been investigated using a surface profiler system, a scanning electron microscopy (SEM), and a microvickers hardness tester. The microstructure, phase composition, and residual stress distribution of the surface layer in AISI 52100 steel after the SFBP treatment have been characterized by means of x-ray diffraction, SEM, and transmission electron microscopy. The results showed that a nanocrystalline surface (NS) layer was formed on the top surface of the SFBP-treated AISI 52100 steel samples. The NS layer is about 2 mu m in thickness with a surface roughness of R (a) = 1.2 mu m, R (y) = 6.7 mu m, R (z) = 6.0 mu m. Phase transitions occurred in the surface of the SFBP-treated samples. Residual compressive stress is obtained at the surface of the SFBP-treated samples. The maximum value of compressive stress appears at the outermost of the surface, and the affection region of the whole surface is about 60 mu m in thickness. A hardened surface layer has been fabricated in the AISI 52100 steel. The thickness of the hardened surface layer is about 70 mu m. The maximum value of hardness occurs at the depth of 20 mu m from the outermost surface.
部门归属	[kong, lingyan ; lao, yuanxia ; xiong, tianying ; li, tiefan] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; kong, ly (reprint author), chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; tyxiong@imr.ac.cn
关键词	Aisi 52100 Steel Nanocrystalline Surface Layer Supersonic Fine Particles Bombarding Surface Treatment Severe Plastic-deformation Fatigue Behavior Metal-alloys Temperature
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/71291
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	L. Y. Kong,Y. X. Lao,T. Y. Xiong,et al. Nanocrystalline Surface Layer on AISI 52100 Steel Induced by Supersonic Fine Particles Bombarding[J]. Journal of Thermal Spray Technology,2013,22(6):1007-1013.
APA	L. Y. Kong,Y. X. Lao,T. Y. Xiong,&T. F. Li.(2013).Nanocrystalline Surface Layer on AISI 52100 Steel Induced by Supersonic Fine Particles Bombarding.Journal of Thermal Spray Technology,22(6),1007-1013.
MLA	L. Y. Kong,et al."Nanocrystalline Surface Layer on AISI 52100 Steel Induced by Supersonic Fine Particles Bombarding".Journal of Thermal Spray Technology 22.6(2013):1007-1013.