An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049

IMR OpenIR

	An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049
	L. J. Chen; Z. G. Wang; G. Yao; J. F. Tian
	2000
发表期刊	Fatigue & Fracture of Engineering Materials & Structures
ISSN	8756-758X
卷号	23 期号:6 页码:509-519
摘要	High-temperature low-cycle fatigue tests with and without a 10-s strain hold period in a cycle were performed on a nickel base superalloy GH4049 under a fully reversed axial total strain control mode. Three creep-fatigue life prediction methods are chosen to analyse the experimental data. These methods are the linear damage summation method (LDS), the strain range partitioning method (SRP) and the strain energy partitioning method (SEP). Their ability to predict creep-fatigue lives of GH4049 at 700, 800 and 850 degrees C has been evaluated. It is found that the SEP method shows an advantage over the SRP method for all the tests under consideration. At 850 degrees C, the LDS and SEP methods give a more satisfactory prediction for creep-fatigue lives. At the temperatures of 700 and 800 degrees C, the SRP and SEP methods can correlate the life data better than the LDS method. In addition, the differences in predictive ability of these methods have also been analysed. The scanning electron microscopy (SEM) examination of fracture surfaces reveals that under creep-fatigue test conditions crack initiation mode is transgranular, while crack propagation mode is either intergranular plus transgranular or entirely intergranular, dependent on test temperature.
部门归属	chinese acad sci, inst met res, state key lab fatigue & fracture mat, shenyang 110015, peoples r china.;chen, lj (reprint author), chinese acad sci, inst met res, state key lab fatigue & fracture mat, 72 wenhua rd, shenyang 110015, peoples r china
关键词	Creep-fatigue Interaction Life Prediction Nickel Base Superalloy Low-cycle Fatigue Temperature 316-stainless-steel Behavior Growth Time
URL	查看原文
WOS记录号	WOS:000089054400005
引用统计	被引频次：19[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/36991
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	L. J. Chen,Z. G. Wang,G. Yao,et al. An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049[J]. Fatigue & Fracture of Engineering Materials & Structures,2000,23(6):509-519.
APA	L. J. Chen,Z. G. Wang,G. Yao,&J. F. Tian.(2000).An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049.Fatigue & Fracture of Engineering Materials & Structures,23(6),509-519.
MLA	L. J. Chen,et al."An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049".Fatigue & Fracture of Engineering Materials & Structures 23.6(2000):509-519.