Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air

IMR OpenIR

	Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air
	S. L. Yang; F. H. Wang; W. T. Wu
	2001
发表期刊	Intermetallics
ISSN	0966-9795
卷号	9 期号:8 页码:741-744
摘要	The cyclic oxidation behavior of a magnetron sputtered NiAl microcrystalline coating was investigated at 1000 degreesC in air by TGA, and SEM in comparison with cast NiAl and NiAlY alloys. Results indicate that, for the cast NiAl alloy, mass loss is observed at about 40 cycles, implying the serious spallation occurred, while no spallation is detected for NiAlY alloy and NiAl coating for the whole test period. It is evident that. the scale adhesion is improved by the microcrystallization and the addition of Y. (C) 2001 Elsevier Science Ltd. All rights reserved.
部门归属	acad sinica, inst met res, state key lab corros & protect, shenyang 110016, peoples r china.;yang, sl (reprint author), acad sinica, inst met res, state key lab corros & protect, shenyang 110016, peoples r china
关键词	Nickel Aluminides Based On Nial Scale Adhesion Al2o3 Scales Oxide Scale Segregation Alpha-al2o3 Morphology Mechanism Growth
URL	查看原文
WOS记录号	WOS:000171006400011
引用统计	被引频次：45[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/36867
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	S. L. Yang,F. H. Wang,W. T. Wu. Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air[J]. Intermetallics,2001,9(8):741-744.
APA	S. L. Yang,F. H. Wang,&W. T. Wu.(2001).Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air.Intermetallics,9(8),741-744.
MLA	S. L. Yang,et al."Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air".Intermetallics 9.8(2001):741-744.