Microstructure and superelasticity of severely deformed TiNi alloy

IMR OpenIR

	Microstructure and superelasticity of severely deformed TiNi alloy
	Z. C. Li; X. K. Zhao; H. Zhang; L. Liu; Y. B. Xu
	2003
发表期刊	Materials Letters
ISSN	0167-577X
卷号	57 期号:5-6 页码:1086-1090
摘要	A Ti-50.4 at.%Ni alloy ingot was prepared and rolled into plate of 1-mm thickness at 1025 K. The hot-rolled plate was cold rolled at room temperature to the extent of 50% reduction in thickness and annealed at 573, 693 and 753 K, respectively. The investigated results revealed that 693 K annealed specimen had a homogeneous nanocrystalline structure with the grain size about 30 nm and showed the best superelasticity. The relation between the microstructure and the superelasticity has been discussed in the present report. (C) 2002 Elsevier Science B.V All rights reserved.
部门归属	chinese acad sci, shenyang natl lab mat sci, met res inst, shenyang 110016, peoples r china. harbin inst technol, sch mat sci & engn, harbin 150001, peoples r china.;li, zc (reprint author), chinese acad sci, shenyang natl lab mat sci, met res inst, shenyang 110016, peoples r china
关键词	Ti-50.4 At.%ni Alloy Cold Roll Anneal Superelasticity Microstructure Memory
URL	查看原文
WOS记录号	WOS:000180262500012
引用统计	被引频次：22[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/35909
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Z. C. Li,X. K. Zhao,H. Zhang,et al. Microstructure and superelasticity of severely deformed TiNi alloy[J]. Materials Letters,2003,57(5-6):1086-1090.
APA	Z. C. Li,X. K. Zhao,H. Zhang,L. Liu,&Y. B. Xu.(2003).Microstructure and superelasticity of severely deformed TiNi alloy.Materials Letters,57(5-6),1086-1090.
MLA	Z. C. Li,et al."Microstructure and superelasticity of severely deformed TiNi alloy".Materials Letters 57.5-6(2003):1086-1090.