| Recrystallization behavior of a two-way cold rolled 12Cr ODS steel | |
| Shen, Jingjie1; Yang, Huilong1; Li, Yanfen2; Kano, Sho1; Matsukawa, Yoshitaka3; Satoh, Yuhki4; Abe, Hiroaki1 | |
| 通讯作者 | Shen, Jingjie(shenjj@tokai.t.u-tokyo.ac.jp) |
| 2019-06-01 | |
| 发表期刊 | FUSION ENGINEERING AND DESIGN
 |
| ISSN | 0920-3796 |
| 卷号 | 143页码:99-105 |
| 摘要 | Recrystallization behavior of a two-way cold rolled 12Cr ODS steel during annealing in the range of 1273-1473 K was systemically investigated by means of scanning electron microscopy, electron backscatter diffraction, transmission electron microscopy, and hardness testing. Results show that original grains with < 110 > axis were rotated to < 111 > axis parallel to normal direction after similar to 60% reduction in thickness. Recovery stage was obvious at 1273 K annealing taking about 100 min, but at higher temperatures it was shortly followed by recrystallization. similar to 84% recrystallization was observed after annealing at 1473 K for 60 min, indicating that the new cold rolling process decreases the recrystallization temperature in comparison with the asfabricated specimen completing recrystallization at 1673 K. In addition, the microtexture evolution was characterized as recrystallization proceeded. The intensity of {111} < 110 > and {111} < 112 > components decreased, while intensive {110} < 001 > component was obtained. Dependence of the stored energy on the orientation of deformed grains is presumed for the reduction of {111} < 110 > and {111} < 112 > components, and oriented growth is probably responsible for the enhancement of {110} < 001 > texture after recrystallization. |
| 关键词 | Oxide dispersion strengthened steels Two-way cold rolling Recrystallization Microstructure Microtexture |
| 资助者 | Ministry of Education, Culture, Sports, Science and Technology in Japan (MEXT) |
| DOI | 10.1016/j.fusengdes.2019.03.113 |
| 收录类别 | SCI |
| 语种 | 英语 |
| 资助项目 | Ministry of Education, Culture, Sports, Science and Technology in Japan (MEXT) |
| WOS研究方向 | Nuclear Science & Technology |
| WOS类目 | Nuclear Science & Technology |
| WOS记录号 | WOS:000470954200013 |
| 出版者 | ELSEVIER SCIENCE SA |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/134170 |
| 专题 | 中国科学院金属研究所 |
| 通讯作者 | Shen, Jingjie |
| 作者单位 | 1.Univ Tokyo, Sch Engn, Nucl Profess Sch, 2-22 Shirakata Shirane, Tokai, Ibaraki 3191188, Japan 2.Chinese Acad Sci, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 3.Tohoku Univ, Inst Mat Res, 2-1-1 Katahira, Sendai, Miyagi 9808577, Japan 4.Hiroshima Inst Technol, Dept Intelligent Mech Engn, Saeki Ku, 2-1-1 Miyake, Hiroshima 7315193, Japan |
| 推荐引用方式 GB/T 7714 | Shen, Jingjie,Yang, Huilong,Li, Yanfen,et al. Recrystallization behavior of a two-way cold rolled 12Cr ODS steel[J]. FUSION ENGINEERING AND DESIGN,2019,143:99-105. |
| APA | Shen, Jingjie.,Yang, Huilong.,Li, Yanfen.,Kano, Sho.,Matsukawa, Yoshitaka.,...&Abe, Hiroaki.(2019).Recrystallization behavior of a two-way cold rolled 12Cr ODS steel.FUSION ENGINEERING AND DESIGN,143,99-105. |
| MLA | Shen, Jingjie,et al."Recrystallization behavior of a two-way cold rolled 12Cr ODS steel".FUSION ENGINEERING AND DESIGN 143(2019):99-105. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论